Varnish for concrete Teknocila 350

Directory > The materials for industrial floors

Varnish for concrete Teknocila 350

Multi-purpose nail Polish on acrylic base for high density concrete.


Введите свои данные

Teknocila 350 - multi-purpose nail for concrete, acrylic-based, highly effective insulating and protective material.


  • To increase the service life of concrete
  • For protection of concrete and other cement surfaces of buildings and infrastructure
  • For concrete floors and walls as a decorative finish


The features and benefits

  • One-component
  • Easy to apply
  • Increases the wear resistance of the surface
  • Making the concrete surface resistant to chlorine
  • Dries very quickly
  • Prevents the formation of cracks in the plaster due to freezing
  • Used as a varnish by pronounced film layer
  • Protects concrete against atmospheric influences penetrate in the concrete in the form of salt
  • High resistance to UV radiation


Usage instructions

The surface must be dry, solid and free from all kinds of foreign particles such as dust, dirt, masli, etc. the Best methods of surface preparation are steam cleaning, a jet of water under high pressure, or grinding.

TEKNOCILA 350 ready to use. Before use, mix well. On the surface, apply by brush or roller with a short NAP manually or automatic dispensers. Do not use on exposed surfaces when the atmospheric precipitation.

20 °C and at least 1 hour (after 30 minutes becomes resistant to dust).


Notes on application / Limitations

  • After using this product should be cleaned using TEKNOTHINNER.
  • Spillage on the skin should be washed with warm water and detergent.
  • The product can irritate the skin. Use protective gloves and goggles. In case of contact with eyes, immediately wash out with warm water and seek medical help.
  • Flammable material should be done at a great distance from open flames, high temperatures, welding and cutting machines and tools.


Transparent liquid


17 l Bucket

Shelf life

12 months in unopened original packaging

The temperature of the fire



0,98 (±0,03) (kg/l)


2 hours


Roller, brush: 0,100 - 0,200 LT/m2

Atomizer: O,150 - 0,250 kg/m2

Temperature range of application

( 5°C) - ( 35°C)

Dry film thickness

135 (±15,00) µm

Full hardening

5 days


In accordance with ASTM O 309-81